<正>表8为n型PERT太阳电池的双面率数据,其产线效率普遍在21%～21.5%。n型PERT太阳电池有两大优势:1)双面率较高,普遍可达到90%左右;2)光致衰减较p型PERC电池低。因此,目前n型PERT电池主要用于双面发电的示范项目中。

关键词(KeyWords)：

Abstract:

Keywords:

基金项目(Foundation):

作者(Author):

参考文献(References)：

• [49]Recamán M,Kuzma I,Li Y,et al.Selective epitaxy as contact passivation approach in bifacial n-type PERT solar cells[A].33rd European Photovoltaic Solar Energy Conference and Exhibition[C].Amsterdam,Netherlands,2017.
• [50]Cornagliotti E,Tous L,Russell R,et al.High efficiency bifacial n-PERT cells with co-plated Ni/Ag contacts for multiwire interconnection[A].SNEC 2017 Scientific Conference[C].Shanghai,China,2017.
• [51]Maria Recamán-Payo,Li Yuandong,Izabela Kuzma-Filipek,et al.Opportunities for silicon epitaxy in bulk crystalline silicon photovoltaics[A].29th European Photovoltaics Solar Energy Conference and Exhibition[C].Amsterdam,Netherlands,2014.
• [52]Feldmann F,Bivour M,Reichel C,et al.Passivated rear contacts for high-efficiency n-type Si solar cellsproviding high interface passivation quality and excellenttransport characteristics[J].Solar Energy Materials&Solar Cells,2014,120:270-274.
• [53]Feldmann F,Bivour M,Reichel C,et al.A passivated rear contact for high-efficiency n-type silicon solar cells enabling high VocS and FF>82%[A].28th European Photovoltaic Solar Energy Conference and Exhibition[C].Paris,France,2013.
• [54]Richter A,Benicka J,Feldmanna F,et al.n-Type Si solar cells with passivating electron contact:Identifying sourcesfor efficiency limitations by wafer thickness and resistivity variation[J].Solar Energy Materials and Solar Cells,2017,173:96-105.
• [55]翟金叶,等.21.5%以上效率Panda-TOPCon双面电池技术研究[A].第17届中国光伏学术大会[C].呼和浩特，2017.
• [56]Descoeudres A,Holman Z C,Barraud L,et al.>21%efficient silicon heterojunction solar cells on n-and p-type wafers compared[J].IEEE Journal of Photovoltaics,2013,3(1):83-89.
• [57]Taguchi M,Yano A,Tohoda S,et al.24.7%record efficiency HIT solar cell onthin silicon wafer[J].IEEE Journal of Photovoltaics,2014,4(1):96-99.
• [58]Yamamoto K,Adachi D,Yoshikawa K,et al.Record-breaking efficiency back-contact heterojunction crystalline Si solar cell and module[A].33rd European PV Solar Energy Conference and Exhibition[C].Amsterdam,Netherlands,2017.
• [59]Meng F,Liu J N,Shen L L,et al.High-quality industrial n-type silicon wafers with an efficiency of over 23%for Si heterojunction solar cells[J].Frontiers in Energy,2017,11(1):78-84.
• [60]Green M A,Emery K,Hishikawa Y,et al.Solar cell efficiency tables(version 47)[J].Progress in Photovoltaics Research and Application,2016,24:3-11.
• [61]Jeyakumar R,Maiti T K,Khader M M,et al.High-efficiency c-Si based interdigitated point contact back heterojunction solar cells[J].Journal of Materials Science:Materials in Electronics,2017,28(13):9697-9703.
• [62]Xu Guanchao,Yang Yang,Zhang Xueling.Large-area(6inch)screen-printed IBC solar cells with efficiency above 24.1%without passivated contacts[A].33rd European Photovoltaic Solar Energy Conference and Exhibition[C].Amsterdam,Netherlands,2017.
• [63]Nakamura J,Katayama H,Koide N,et al.Development of hetero-junction back contact Si solar cells[A].40th IEEEPhotovoltaic Specialist Conference[C].Denver,Colorado,2014.
• [64]Yoshikawa K,Yoshida W,Irie T,et al.Exceeding conversion efficiency of 26%by heterojunction interdigitated back contact solar cell with thin film Si technology[J].Solar Energy Materials and Solar Cells,2017,173:37-42.
• [65]应用异质结和背接触技术，日本Kaneka公司HBC电池效率达到创纪录的26.33%[EB/OL].http://blog.sina.com.cn/s/blog_7165948f0102wtle.html,2016-09.
• [66]Newman B K,Bende E E,Aken B B V,et al.Manipulating reverse current in 21%n-MWT cells[A].31st European Photovoltaic Solar Energy Conference and Exhibition[C].Hamburg,Germany,2015.
• [67]Clement F,Menkoe M,Kubera T,et al.Industrially feasible multi-crystalline metal wrap through(MWT)silicon solar cells exceeding 16%efficiency[J].Solar energy materials and solar cells,2009,93:1051-1055.
• [68]Clement F,Lutsch M,Kubera T,et al.Processing and comprehensive characterisation of screen-printed mc-Si Metal Wrap Through(MWT)solar cells[A].22nd European Photovoltaic Solar Energy Conference[C].Milano,2007.
• [69]Clement F,Menkoe M,Erath D,et al.High throughput viametallization technique for multi-crystalline metal wrap through(MWT)silicon solar cells exceeding 16%efficiency[J].Solar Energy Materials and Solar Cells,2010,94:51-56.
• [70]Guillevin N,Heurtault B J B,Geerligs L J,et al.Development towards 20%efficient Si MWT solar cells for low-cost industrial production[J].Energy Procedia,2011,8:9-16.
• [71]Inomata Y,Fukui K,Shirasawa K.Surface texturing of large area multicrystalline silicon solar cells using reactive ion etching method[J].Solar Energy Materials and Solar Cells,1997,48:237-242.
• [72]Yoo J,Yu G,Yi J.Large-area multicrystalline silicon solar cell fabrication using reactive ion etching(RIE)[J].Solar Energy Materials and Solar Cells,2011,95:2-6.
• [73]Kumaai A.Texturization using metal catalyst wet chemical etching for multicrystalline diamond wire sawn wafer[J].Solar Energy Materials and Solar Cells,2015,133:216-222.
• [74]Cao F,Chen K,Zhang J,et al.Next-generation multicrystalline silicon solar cells:Diamond-wire sawing,nano-texture and high efficiency[J].Solar Energy Materials and Solar Cells,2015,141:132-138.